Seramik Filtre Cff

17 Eylül Seramik Filtre Cff

Cff Seramik Filtre, Rusya, Orta Doğu ve Güneydoğu Asya’daki büyük alüminyum işleme işletmelerinin üretiminde yaygın olarak kullanılmaktadır.
During use, it is not only necessary to remove the aluminum melt inclusions, but also to avoid the blockage of the Ceramic Filter Cff and improve the service life of the CFF.

The melt is not filtered, which contains a large number of inclusions of different sizes. The coarse inclusions often form micropores first, which promotes the propagation of cracks, so the performance of the alloy is reduced.
If the melt is filtered, the inclusions in the alloy will decrease, the average spacing will increase, and the plastic zone at the crack tip will expand, which will lead to an increase in the resistance to crack propagation, which ultimately manifests as the performance of the alloy.

The filtering principle of Ceramic Filter Cff
Alüminyum alaşımı eriyiğinin süzülmesi, yüzey süzme ve iç süzme işlemlerini içerir.
Yüzey filtrasyonu, katı kirliliklerin esas olarak filtre malzemesinin yüzeyinde birikmesi anlamına gelir.
Internal filtration means that the molten aluminum carries inclusions in the Köpük Seramik Filtre media along the tortuous channels and pores, which are directly intercepted, adsorbed, deposited, etc., collide with the pore wall and firmly adhere to the pore wall.
Filtrasyon ilerledikçe, gözeneklerin etkin filtrasyon bölümü kademeli olarak azalır, geçirgenlik düşer ve filtrasyon hassasiyeti artar.
Seramik Filtre (Cff) ve derin yatak filtrasyonu iç filtrasyona dahilken, boru tipi filtrasyon ise kirletici maddelerin hem yüzeyde hem de iç kısımda tutulmasına dayalı bir yöntemdir.

When the aluminum alloy melt is not filtered, a large number of inclusions will increase the viscosity of the aluminum alloy liquid and reduce the fluidity.During solidification, the interdendritic feeding channel is easily blocked, forming microscopic shrinkage and porosity.
At the same time, these impurity spots will also adsorb bubbles, form pores in the sample, become the source of microcracks, and reduce the performance of the alloy.
In addition, because the inclusions are mostly distributed in the grain boundaries after the alloy is solidified, the interface bonding force between the grains is reduced, resulting in intergranular fracture after the sample is stressed, which can be observed from the oxide film of the dendritic adhesion on the fracture Or inclusions can be confirmed. Metal Foam Filter Factory email: sales@adtechamm.com

The process by which inclusions in the matrix affect the fracture of the aluminum alloy specimen
Numune çekme kuvvetine maruz kaldığında, çatlak ön kenarında şiddetli bir yoğun gerilme oluşur. Çekme gerilimi akma mukavemetini aştığında, önce çatlak ucunun yakınında plastik deformasyon meydana gelir ve bir plastik bölge oluşur; bu da gerilme gevşemesine ve çatlak ucunun körelmesine yol açar.
Plastik bölge genişledikçe, çatlağın ön ucundaki kalıntılar plastik bölgeye girer.
Kapsamlar ile matris arasındaki bağlanma kuvveti nispeten zayıf olduğundan, çekme geriliminin etkisiyle kapsamlar matristen ayrılır ve ilk mikro gözenekleri oluşturur.
Yük artırılmaya devam edildikçe, çatlak ucu ile mikro delik arasındaki iç daralma şiddetlenir; bu da çatlak ucunun ve mikro deliğin hızla birleşmesine neden olur ve çatlak ileriye doğru genişlemeye başlar.
Bu nedenle, kalıntılar ilk mikro gözeneklerin oluşumuna elverişlidir ve çatlakların yayılmasında daha büyük bir etkiye sahiptir.

İlgili yazılar:

Gözenekli Seramik Filtre Fabrikası Alümina Seramik Köpük Filtre Satışı Rus Alüminyum Seramik Döküm Filtresi Satışı Döküm Filtre Fabrikası Dökümhane İçin Seramik Filtre Zirkonya Filtre Fabrikası Seramik Köpük Filtre Tedarikçileri Döküm Filtresi Fabrikası Seramik Filtre Köpüğü Döküm İçin Seramik Köpük Filtre Zirkonya Cff 20 Ppi Cff Alümina Seramik Filtrasyon