Ceramic Filter Cff | Adtech China

17 сентября Керамический фильтр Cff

Posted at 08:30h in Керамический пенофильтр by AdTech 0 Comments

0 Likes

Керамический фильтр Cff широко применяется на крупных предприятиях по переработке алюминия в России, на Ближнем Востоке и в Юго-Восточной Азии.
During use, it is not only necessary to remove the aluminum melt inclusions, but also to avoid the blockage of the Ceramic Filter Cff and improve the service life of the CFF.

The melt is not filtered, which contains a large number of inclusions of different sizes. The coarse inclusions often form micropores first, which promotes the propagation of cracks, so the performance of the alloy is reduced.
If the melt is filtered, the inclusions in the alloy will decrease, the average spacing will increase, and the plastic zone at the crack tip will expand, which will lead to an increase in the resistance to crack propagation, which ultimately manifests as the performance of the alloy.

The filtering principle of Ceramic Filter Cff
Фильтрация расплава алюминиевого сплава включает в себя поверхностную и внутреннюю фильтрацию.
Поверхностная фильтрация означает, что твердые примеси в основном оседают на поверхности фильтрующего материала.
Internal filtration means that the molten aluminum carries inclusions in the Пенокерамический фильтр media along the tortuous channels and pores, which are directly intercepted, adsorbed, deposited, etc., collide with the pore wall and firmly adhere to the pore wall.
По мере продвижения процесса фильтрации эффективная фильтрующая площадь пор постепенно уменьшается, проницаемость снижается, а точность фильтрации повышается.
Керамический фильтр Cff и фильтрация с глубоким слоем относятся к внутренней фильтрации, тогда как трубчатая фильтрация предполагает двойное улавливание примесей — как на поверхности, так и внутри.

When the aluminum alloy melt is not filtered, a large number of inclusions will increase the viscosity of the aluminum alloy liquid and reduce the fluidity.During solidification, the interdendritic feeding channel is easily blocked, forming microscopic shrinkage and porosity.
At the same time, these impurity spots will also adsorb bubbles, form pores in the sample, become the source of microcracks, and reduce the performance of the alloy.
In addition, because the inclusions are mostly distributed in the grain boundaries after the alloy is solidified, the interface bonding force between the grains is reduced, resulting in intergranular fracture after the sample is stressed, which can be observed from the oxide film of the dendritic adhesion on the fracture Or inclusions can be confirmed. Metal Foam Filter Factory email: sales@adtechamm.com

The process by which inclusions in the matrix affect the fracture of the aluminum alloy specimen
Когда образец подвергается растягивающей нагрузке, на переднем крае трещины возникают сильные сосредоточенные напряжения. Когда растягивающее напряжение превышает предел текучести, вблизи вершины трещины сначала возникает пластическая деформация, в результате чего образуется пластическая зона, что приводит к релаксации напряжений и скруглению вершины трещины.
По мере расширения пластической зоны включения, расположенные в передней части трещины, попадают в эту зону.
Поскольку сила сцепления между включениями и матрицей относительно слабая, под действием растягивающего напряжения включения отделяются от матрицы, образуя начальные микропоры.
По мере дальнейшего увеличения нагрузки внутреннее сужение между вершиной трещины и микроотверстием усиливается, что приводит к быстрому сближению вершины трещины и микроотверстия, и трещина начинает расширяться вперед.
Таким образом, включения способствуют образованию начальных микропор и оказывают более значительное влияние на распространение трещин.