{"id":3061,"date":"2018-02-06T03:44:51","date_gmt":"2018-02-06T03:44:51","guid":{"rendered":"http:\/\/www.adtechamm.com\/?p=3061"},"modified":"2018-02-06T03:44:51","modified_gmt":"2018-02-06T03:44:51","slug":"study-solidification-defects-aluminum-alloy","status":"publish","type":"post","link":"https:\/\/www.adtechamm.com\/id\/study-solidification-defects-aluminum-alloy\/","title":{"rendered":"STUDI TENTANG CACAT PENGERASAN PADA PADUAN ALUMINIUM"},"content":{"rendered":"

STUDI TENTANG CACAT PENGERASAN PADA PADUAN ALUMINIUM<\/p>\n

Sinkronisasi lapisan oksida ganda
\n(1) Gelombang pecah terbentuk akibat turbulensi di permukaan. (2) Kedua sisi lapisan oksida yang tidak terbasahi saling bersentuhan.
\n(3) Lapisan oksida ganda terbenam ke dalam cairan sebagai cacat berbentuk retakan.<\/p>\n

 <\/p>\n

\"Sinkronisasi<\/a><\/p>\n

 <\/p>\n

Cacat Entrainment
\nTurbulensi permukaan yang menyebabkan terlepasnya lapisan ganda dan gelembung-gelembung yang menyertainya.
\nA \u2013 B:- Gelembung-gelembung kecil yang terbawa membentuk pori-pori pada bifilm.
\nC dan D:- Gelembung-gelembung besar memiliki daya apung, sehingga membentuk jejak sebelum tertangkap di tempat lain atau akhirnya terlepas.<\/p>\n

 <\/p>\n

\"Cacat<\/p>\n

 <\/p>\n

Cacat Entrainment<\/p>\n

 <\/p>\n

\"Cacat<\/p>\n

 <\/p>\n

Perkembangan bifilm<\/p>\n

Penggulungan
\nBifilm dipukul-pukul dan digulung menjadi bentuk yang padat dan berliku-liku.
\nJika cairan di bawah permukaan mengalami turbulensi skala besar, Re > 2000<\/p>\n

Membentangkan
\nPengisian cetakan telah selesai, Re<2000
\nPresipitasi gas melalui lapisan alumina
\nPembentukan pori interdendritik
\nMenentukan sifat-sifat bahan cor<\/p>\n

\"Membentangkan\"<\/p>\n

Pengaruh Kadar Hidrogen dan Jarak Antara Cabang Dendrit<\/p>\n

Kiri Bawah:
\nInflasi mikro<\/p>\n

Bawah Kanan:
\nPada waktu pengendapan yang singkat, kepadatan pori meningkat seiring dengan meningkatnya kandungan hidrogen.<\/p>\n

Kiri Atas:
\nKelompok-kelompok pori yang berjumlah banyak.<\/p>\n

Kanan Atas:
\nPada waktu pengendapan yang lebih lama, kepadatan pori menurun seiring dengan meningkatnya kandungan hidrogen.<\/p>\n

 <\/p>\n

\"<\/p>\n

 <\/p>\n

Masalah yang Disebabkan oleh Lapisan yang Terendam Air
\nMasalah Pemesinan
\nOksida jauh lebih keras daripada logam itu sendiri, sehingga menyebabkan gesekan saat pemesinan, yang meninggalkan alur-alur yang tidak sedap dipandang.
\n``` Ujung tajam alat sering kali retak atau tumpul akibat menghadapi masalah-masalah semacam itu.```.<\/p>\n

Ketatannya Terhadap Kebocoran
\n``` Untuk coran berdinding tipis dengan ketebalan 5 mm atau kurang, cacat lapisan tipis dapat meluas dari satu dinding ke dinding lainnya melintasi rongga cetakan, sehingga menghubungkan rongga coran dan permukaannya melalui jalur kebocoran.
\nCacat gelembung sangat merepotkan dalam hal kedap bocor, karena cacat tersebut pasti bermula di salah satu permukaan coran dan terhubung ke permukaan di atasnya.
\nKelancaran
\nKekentalan lelehan bersih selalu lebih tinggi daripada lelehan yang terkontaminasi, dan dapat dituang pada suhu yang lebih rendah.
\nManfaat kumulatifnya sangat berharga.<\/p>\n

 <\/p>\n

Pengaruh terhadap Sifat Mekanik: UTS dan Perpanjangan
\n| Jarak antar lengan dendrit meningkat
\nKekuatan Menurun
\n\u202f\u202fPenurunan Perpanjangan
\nKekuatan patah
\n\u202f\u202fPenurunan
\nSifat kelelahan menurun
\nKorosi
\nLubang korosi dan serat korosi umumnya terjadi pada cacat pengecoran yang terbawa.<\/p>\n

\"cacat<\/p>\n

Penghapusan cacat pengendapan
\nPenghilangan Gas<\/p>\n

\"berbagai
\nDiagram skematis yang menggambarkan berbagai tahap penghilangan gas<\/p>\n

 <\/p>\n

Penghilangan Gas
\nUntuk menghilangkan hidrogen dari aluminium cair, proses penghilangan gas sangatlah penting.
\n``` Flux, gas pembersih, degassing vakum, dan getaran ultrasonik dapat digunakan sebagai metode degassing. Metode yang paling umum digunakan adalah dengan mengalirkan gas inert atau reaktif dari dekat bagian bawah tungku.
\n``` Gas pembersih biasanya berupa Ar atau campuran dari gas-gas tersebut. Selama melewati cairan logam, gelembung-gelembung\u2014yang pada awalnya memiliki kandungan hidrogen rendah\u2014menyerap hidrogen dari cairan logam dan kemudian keluar ke permukaan.```.
\n```Suhu leleh, ukuran gelembung gas, dan komposisi gas merupakan faktor-faktor penting dalam metode penghilangan gas ini. Kelarutan hidrogen meningkat dua kali lipat ketika suhu aluminium cair naik sebesar 60 \u00b0C.```.
\n```Ukuran gelembung gas menentukan rasio luas\/volume (A\/V). Untuk efisiensi degassing yang tinggi, nilai A\/V harus dimaksimalkan, dan gelembung berukuran kurang dari 5 mm adalah yang paling efektif.```.<\/p>\n

Penghapusan inklusi
\n\"CACAT
\nIlustrasi skematis media penyaring<\/p>\n

 <\/p>\n

 <\/p>\n

Penghapusan inklusi
\nInklusi seperti aluminium oksida dan Mg berasal dari ingot atau reaksi dengan oksigen di udara atau kelembapan selama proses peleburan dan pengecoran.
\n```Proses sedimentasi, flotasi, dan filtrasi di dalam tungku digunakan oleh industri pengecoran untuk menghilangkan inklusi-inklusi tersebut.```.
\n```Setelah mencapai permukaan, zat-zat tersebut dapat dihilangkan dengan cara disaring. Namun, fluks-fluks ini mengandung unsur-unsur berbahaya seperti Cl, F, atau P.```.
\nFlux itu sendiri dapat menjadi inklusi dalam hasil coran jika tetap tertinggal dalam cairan logam setelah proses perlakuan. Setelah dilakukan pembersihan selama proses peleburan, filter yang terpasang di dalam cetakan dapat membantu menghilangkan inklusi seperti flux, partikel keramik, atau lapisan oksida selama proses pengisian.
\n``` Inklusi dapat terperangkap di permukaan depan atau permukaan masuk filter, dan membentuk lapisan-lapisan kue filter.<\/p>\n

Penghilangan lapisan film yang terbawa
\nSaat terendam, lapisan tersebut terus tumbuh dengan mengonsumsi gas-gas yang tersimpan: oksigen untuk membentuk oksida, nitrogen untuk membentuk nitrida, sedangkan gas-gas lainnya larut dalam larutan
\nPada akhirnya, semua gas akan habis, dan dampak paling merusak yang disebabkan oleh lapisan tersebut\u2014seperti kebocoran, pembentukan gelembung, rongga, serta retakan\u2014akan teratasi.
\n```Penonaktifan otomatis lapisan yang terbawa ini biasanya terjadi pada kasus-kasus di mana logam tersebut dikenai tekanan (pencetakan dengan penekanan (50\u2013150 MPa), penekanan isostatik panas (200 MPa), bahkan beberapa manfaat juga diperoleh dalam pencetakan pasir dengan tekanan sedang sebesar hanya 0,7 MPa).```.<\/p>\n

 <\/p>","protected":false},"excerpt":{"rendered":"

STUDY OF SOLIDIFICATION DEFECTS OF ALUMINUM ALLOY Entrainment of a double oxide film (1)A breaking wave is formed by surface turbulence.(2)The two un-wetted sides of the oxide films contact each other. (3)A double oxide film is submerged into the bulk liquid as a crack like…<\/p>","protected":false},"author":1,"featured_media":3064,"comment_status":"open","ping_status":"open","sticky":false,"template":"","format":"standard","meta":[],"categories":[52],"tags":[800,801],"yoast_head":"\nDEFECTS OF ALUMINUM ALLOY-AdTech Metallurgical Materials Co.,Ltd.<\/title>\n<meta name=\"description\" content=\"STUDY OF SOLIDIFICATION DEFECTS OF ALUMINUM ALLOY (1)A breaking wave is formed by surface turbulence. (2)The two un-wetted sides of the oxide...\" \/>\n<meta name=\"robots\" content=\"index, follow, max-snippet:-1, max-image-preview:large, max-video-preview:-1\" \/>\n<link rel=\"canonical\" href=\"https:\/\/www.adtechamm.com\/id\/study-solidification-defects-aluminum-alloy\/\" \/>\n<meta property=\"og:locale\" content=\"id_ID\" \/>\n<meta property=\"og:type\" content=\"article\" \/>\n<meta property=\"og:title\" content=\"DEFECTS OF ALUMINUM ALLOY-AdTech Metallurgical Materials Co.,Ltd.\" \/>\n<meta property=\"og:description\" content=\"STUDY OF SOLIDIFICATION DEFECTS OF ALUMINUM ALLOY (1)A breaking wave is formed by surface turbulence. (2)The two un-wetted sides of the oxide...\" \/>\n<meta property=\"og:url\" content=\"https:\/\/www.adtechamm.com\/id\/study-solidification-defects-aluminum-alloy\/\" \/>\n<meta property=\"og:site_name\" content=\"Adtech China\" \/>\n<meta property=\"article:publisher\" content=\"https:\/\/www.facebook.com\/avril.allen.3994\" \/>\n<meta property=\"article:author\" content=\"https:\/\/www.facebook.com\/profile.php?id=100058838456679\" \/>\n<meta property=\"article:published_time\" content=\"2018-02-06T03:44:51+00:00\" \/>\n<meta property=\"og:image\" content=\"https:\/\/www.adtechamm.com\/wp-content\/uploads\/2018\/02\/2.3.jpg\" \/>\n\t<meta property=\"og:image:width\" content=\"912\" \/>\n\t<meta property=\"og:image:height\" content=\"619\" \/>\n\t<meta property=\"og:image:type\" content=\"image\/jpeg\" \/>\n<meta name=\"author\" content=\"AdTech\" \/>\n<meta name=\"twitter:card\" content=\"summary_large_image\" \/>\n<meta name=\"twitter:creator\" content=\"@AdTech_China\" \/>\n<meta name=\"twitter:site\" content=\"@AdTech_China\" \/>\n<meta name=\"twitter:label1\" content=\"Ditulis oleh\" \/>\n\t<meta name=\"twitter:data1\" content=\"AdTech\" \/>\n\t<meta name=\"twitter:label2\" content=\"Estimasi waktu membaca\" \/>\n\t<meta name=\"twitter:data2\" content=\"4 menit\" \/>\n<script type=\"application\/ld+json\" class=\"yoast-schema-graph\">{\"@context\":\"https:\/\/schema.org\",\"@graph\":[{\"@type\":\"WebPage\",\"@id\":\"https:\/\/www.adtechamm.com\/study-solidification-defects-aluminum-alloy\/\",\"url\":\"https:\/\/www.adtechamm.com\/study-solidification-defects-aluminum-alloy\/\",\"name\":\"DEFECTS OF ALUMINUM ALLOY-AdTech Metallurgical Materials Co.,Ltd.\",\"isPartOf\":{\"@id\":\"https:\/\/www.adtechamm.com\/#website\"},\"datePublished\":\"2018-02-06T03:44:51+00:00\",\"dateModified\":\"2018-02-06T03:44:51+00:00\",\"author\":{\"@id\":\"https:\/\/www.adtechamm.com\/#\/schema\/person\/3e620479604c811a3f1f75bb70841291\"},\"description\":\"STUDY OF SOLIDIFICATION DEFECTS OF ALUMINUM ALLOY (1)A breaking wave is formed by surface turbulence. (2)The two un-wetted sides of the oxide...\",\"breadcrumb\":{\"@id\":\"https:\/\/www.adtechamm.com\/study-solidification-defects-aluminum-alloy\/#breadcrumb\"},\"inLanguage\":\"id\",\"potentialAction\":[{\"@type\":\"ReadAction\",\"target\":[\"https:\/\/www.adtechamm.com\/study-solidification-defects-aluminum-alloy\/\"]}]},{\"@type\":\"BreadcrumbList\",\"@id\":\"https:\/\/www.adtechamm.com\/study-solidification-defects-aluminum-alloy\/#breadcrumb\",\"itemListElement\":[{\"@type\":\"ListItem\",\"position\":1,\"name\":\"\u9996\u9875\",\"item\":\"https:\/\/www.adtechamm.com\/\"},{\"@type\":\"ListItem\",\"position\":2,\"name\":\"STUDY OF SOLIDIFICATION DEFECTS OF ALUMINUM ALLOY\"}]},{\"@type\":\"WebSite\",\"@id\":\"https:\/\/www.adtechamm.com\/#website\",\"url\":\"https:\/\/www.adtechamm.com\/\",\"name\":\"Adtech China\",\"description\":\"Alumina ceramic foam filter, aluminum degassing\",\"potentialAction\":[{\"@type\":\"SearchAction\",\"target\":{\"@type\":\"EntryPoint\",\"urlTemplate\":\"https:\/\/www.adtechamm.com\/?s={search_term_string}\"},\"query-input\":\"required name=search_term_string\"}],\"inLanguage\":\"id\"},{\"@type\":\"Person\",\"@id\":\"https:\/\/www.adtechamm.com\/#\/schema\/person\/3e620479604c811a3f1f75bb70841291\",\"name\":\"AdTech\",\"description\":\"Alumina ceramic foam filter & degassing unit\",\"sameAs\":[\"https:\/\/www.adtechamm.com\/\",\"https:\/\/www.facebook.com\/profile.php?id=100058838456679\",\"https:\/\/www.linkedin.com\/in\/--618200221\/\",\"https:\/\/youtube.com\/@adtechamm2577\",\"https:\/\/www.tumblr.com\/adtechmetallurgicalmaterials\"]}]}<\/script>\n<!-- \/ Yoast SEO plugin. -->","yoast_head_json":{"title":"Cacat pada Paduan Aluminium - AdTech Metallurgical Materials Co., Ltd.","description":"STUDI TENTANG CACAT PENGERASAN PADA PADUAN ALUMINIUM (1) Gelombang pecah terbentuk akibat turbulensi permukaan. (2) Kedua sisi lapisan oksida yang tidak terbasahi...","robots":{"index":"index","follow":"follow","max-snippet":"max-snippet:-1","max-image-preview":"max-image-preview:large","max-video-preview":"max-video-preview:-1"},"canonical":"https:\/\/www.adtechamm.com\/id\/study-solidification-defects-aluminum-alloy\/","og_locale":"id_ID","og_type":"article","og_title":"DEFECTS OF ALUMINUM ALLOY-AdTech Metallurgical Materials Co.,Ltd.","og_description":"STUDY OF SOLIDIFICATION DEFECTS OF ALUMINUM ALLOY (1)A breaking wave is formed by surface turbulence. (2)The two un-wetted sides of the oxide...","og_url":"https:\/\/www.adtechamm.com\/id\/study-solidification-defects-aluminum-alloy\/","og_site_name":"Adtech China","article_publisher":"https:\/\/www.facebook.com\/avril.allen.3994","article_author":"https:\/\/www.facebook.com\/profile.php?id=100058838456679","article_published_time":"2018-02-06T03:44:51+00:00","og_image":[{"width":912,"height":619,"url":"https:\/\/www.adtechamm.com\/wp-content\/uploads\/2018\/02\/2.3.jpg","type":"image\/jpeg"}],"author":"AdTech","twitter_card":"summary_large_image","twitter_creator":"@AdTech_China","twitter_site":"@AdTech_China","twitter_misc":{"Ditulis oleh":"AdTech","Estimasi waktu membaca":"4 menit"},"schema":{"@context":"https:\/\/schema.org","@graph":[{"@type":"WebPage","@id":"https:\/\/www.adtechamm.com\/study-solidification-defects-aluminum-alloy\/","url":"https:\/\/www.adtechamm.com\/study-solidification-defects-aluminum-alloy\/","name":"Cacat pada Paduan Aluminium - AdTech Metallurgical Materials Co., Ltd.","isPartOf":{"@id":"https:\/\/www.adtechamm.com\/#website"},"datePublished":"2018-02-06T03:44:51+00:00","dateModified":"2018-02-06T03:44:51+00:00","author":{"@id":"https:\/\/www.adtechamm.com\/#\/schema\/person\/3e620479604c811a3f1f75bb70841291"},"description":"STUDI TENTANG CACAT PENGERASAN PADA PADUAN ALUMINIUM (1) Gelombang pecah terbentuk akibat turbulensi permukaan. (2) Kedua sisi lapisan oksida yang tidak terbasahi...","breadcrumb":{"@id":"https:\/\/www.adtechamm.com\/study-solidification-defects-aluminum-alloy\/#breadcrumb"},"inLanguage":"id","potentialAction":[{"@type":"ReadAction","target":["https:\/\/www.adtechamm.com\/study-solidification-defects-aluminum-alloy\/"]}]},{"@type":"BreadcrumbList","@id":"https:\/\/www.adtechamm.com\/study-solidification-defects-aluminum-alloy\/#breadcrumb","itemListElement":[{"@type":"ListItem","position":1,"name":"\u9996\u9875","item":"https:\/\/www.adtechamm.com\/"},{"@type":"ListItem","position":2,"name":"STUDY OF SOLIDIFICATION DEFECTS OF ALUMINUM ALLOY"}]},{"@type":"WebSite","@id":"https:\/\/www.adtechamm.com\/#website","url":"https:\/\/www.adtechamm.com\/","name":"Adtech Tiongkok","description":"Filter busa keramik alumina, penghilangan gas dari aluminium","potentialAction":[{"@type":"SearchAction","target":{"@type":"EntryPoint","urlTemplate":"https:\/\/www.adtechamm.com\/?s={search_term_string}"},"query-input":"required name=search_term_string"}],"inLanguage":"id"},{"@type":"Person","@id":"https:\/\/www.adtechamm.com\/#\/schema\/person\/3e620479604c811a3f1f75bb70841291","name":"AdTech","description":"Filter busa keramik alumina & unit penghilang gas","sameAs":["https:\/\/www.adtechamm.com\/","https:\/\/www.facebook.com\/profile.php?id=100058838456679","https:\/\/www.linkedin.com\/in\/--618200221\/","https:\/\/youtube.com\/@adtechamm2577","https:\/\/www.tumblr.com\/adtechmetallurgicalmaterials"]}]}},"_links":{"self":[{"href":"https:\/\/www.adtechamm.com\/id\/wp-json\/wp\/v2\/posts\/3061"}],"collection":[{"href":"https:\/\/www.adtechamm.com\/id\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/www.adtechamm.com\/id\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/www.adtechamm.com\/id\/wp-json\/wp\/v2\/users\/1"}],"replies":[{"embeddable":true,"href":"https:\/\/www.adtechamm.com\/id\/wp-json\/wp\/v2\/comments?post=3061"}],"version-history":[{"count":1,"href":"https:\/\/www.adtechamm.com\/id\/wp-json\/wp\/v2\/posts\/3061\/revisions"}],"predecessor-version":[{"id":3070,"href":"https:\/\/www.adtechamm.com\/id\/wp-json\/wp\/v2\/posts\/3061\/revisions\/3070"}],"wp:featuredmedia":[{"embeddable":true,"href":"https:\/\/www.adtechamm.com\/id\/wp-json\/wp\/v2\/media\/3064"}],"wp:attachment":[{"href":"https:\/\/www.adtechamm.com\/id\/wp-json\/wp\/v2\/media?parent=3061"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/www.adtechamm.com\/id\/wp-json\/wp\/v2\/categories?post=3061"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/www.adtechamm.com\/id\/wp-json\/wp\/v2\/tags?post=3061"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}